چکیده مقاله
A Mixed system of bulky α-diimine nickel (MNi) was prepared and activated by methylaluminoxane. The catalytic system MNi was used for propylene polymerization under various conditions. The highest polymer yield and Mv of polypropylene were obtained about 0.354 g and 1.24 × 105 respectively, at 20 °C, 60 min and +4 bars. The Tg of obtained polypropylenes was about –35 °C while resulting polypropylene at temperature of 60 °C was very soft with high tack. Structural analysis of polypropylene (PP-MNi) produced by MNi was carried out by 13C NMR technique. Sequences of ethylene, propylene, ethylene-propylene (EP) and inverted propylene in PP-MNi were identified and those were compared with the sequences of reported ethylene-propylene copolymers which had been synthesized using constrained geometry catalyst and vanadium-based Ziegler-Natta catalyst.
نحوه استناد به مقاله
در صورتی که می خواهید به این مقاله در اثر پژوهشی خود ارجاع دهید، می توانید از متن زیر در بخش منابع و مراجع بهره بگیرید :
Hamid Pourtaghi-Zahed؛Gholam Hossein Zohuri؛ ۱۳۹۵، Synthesis and structural analysis of rubber like polypropylene produced by bulky α-diimine nickel in comparison with conventional ethylene-propylene rubber and its industrial applications، پنجمین کنفرانس بین المللی پژوهش در علوم و تکنولوژی، https://scholar.conference.ac:443/index.php/download/file/9960-Synthesis-and-structural-analysis-of-rubber-like-polypropylene-produced
در داخل متن نیز هر جا به عبارت و یا دستاوردی از این مقاله اشاره شود پس از ذکر مطلب، در داخل پرانتز، مشخصات زیر نوشته شود.
(Hamid Pourtaghi-Zahed؛Gholam Hossein Zohuri؛ ۱۳۹۵)